STS is an escrow service that protects both buyers and suppliers. Funds are held securely by Made-in-China.com until order terms (e.g., delivery, quality) are fulfilled
| Customization: | Available |
|---|---|
| Certification: | ISO, CE, CNAS |
| Color: | Yellow |
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
Payment Guarantee
Platform-protected payments with refund support for eligible order issues.
Platform Logistics
Inspection Service
After-Sales & Dispute Handling
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
| No. | Item | Description | ||||||||||
| 1 | Description | The yellow-green (two-color) heat-shrinkable tube is made of environmentally friendly polyolefin material, yellow-green two-color co-extrusion, and processed by the spoke clothing industry. It is widely used in the identification of the ground wire in the wire harness or cable, the identification of the special wire small busbar or the pipeline, etc. |
||||||||||
| 2 | Shrinkage ratio | 2:1, 3:1 | ||||||||||
| 3 | Shrinkage Temperature | 85ºC~125ºC | ||||||||||
| 4 | Working Temperature | -55ºC~125ºC | ||||||||||
| 5 | Environmental Standard | RoHS | ||||||||||
| 6 | Standard Color | yellow-green | ||||||||||
| Size (mm) |
Before Shrink (mm) |
Before Shrink (mm) |
Package (m/roll) |
|||||||||
| Inner Diameter | Wall Thickness | Inner Diameter | Wall Thickness | |||||||||
| Φ1.0 | 1.5±0.3 | 0.15±0.08 | ≤0.65 | 0.28±0.10 | 200 | |||||||
| Φ1.5 | 2.0±0.3 | 0.18±0.08 | ≤0.85 | 0.32±0.10 | 200 | |||||||
| Φ2.0 | 2.5±0.3 | 0.18±0.08 | ≤1.00 | 0.4±0.10 | 200 | |||||||
| Φ2.5 | 3.0±0.3 | 0.18±0.08 | ≤1.30 | 0.4±0.10 | 200 | |||||||
| Φ3.0 | 3.5±0.4 | 0.18±0.08 | ≤1.50 | 0.4±0.10 | 200 | |||||||
| Φ3.5 | 4.0±0.4 | 0.22±0.08 | ≤1.80 | 0.42±0.10 | 200 | |||||||
| Φ4.0 | 4.5±0.4 | 0.25±0.08 | ≤2.00 | 0.45±0.10 | 200 | |||||||
| Φ5.0 | 5.5±0.4 | 0.25±0.08 | ≤2.50 | 0.55±0.10 | 100 | |||||||
| Φ6.0 | 6.5±0.4 | 0.28±0.08 | ≤3.00 | 0.55±0.10 | 100 | |||||||
| Φ8.0 | 8.5±0.5 | 0.28±0.10 | ≤4.00 | 0.6±0.10 | 100 | |||||||
| Φ10 | 10.5±0.5 | 0.3±0.10 | ≤5.00 | 0.6±0.10 | 100 | |||||||
| Φ12 | 12.5±0.5 | 0.3±0.10 | ≤6.00 | 0.65±0.10 | 100 | |||||||
| Φ14 | 14.5±0.5 | 0.35±0.12 | ≤7.00 | 0.7±0.10 | 100 | |||||||
| Φ15 | 15.5±0.6 | 0.4±0.12 | ≤7.50 | 0.75±0.10 | 100 | |||||||
| Φ16 | 17.0±0.6 | 0.4±0.12 | ≤8.00 | 0.75±0.10 | 100 | |||||||
| Φ18 | 19.0±0.7 | 0.4±0.15 | ≤9.00 | 0.8±0.10 | 100 | |||||||
| Φ20 | 22.0±0.7 | 0.4±0.15 | ≤10.00 | 0.82±0.10 | 100 | |||||||
| Φ22 | 24.0±0.7 | 0.4±0.15 | ≤11.00 | 0.82±0.10 | 100 | |||||||
| Φ25 | 26.0±0.7 | 0.55±0.15 | ≤12.50 | 1±0.15 | 50 | |||||||
| Φ28 | 29.0±0.7 | 0.55±0.15 | ≤14.00 | 1±0.15 | 50 | |||||||
| Φ30 | 31.5±0.7 | 0.55±0.15 | ≤15.00 | 1.05±0.15 | 50 | |||||||
| Φ35 | 36.5±0.7 | 0.55±0.15 | ≤17.50 | 1.15±0.15 | 50 | |||||||
| Φ40 | 41.5±0.7 | 0.55±0.15 | ≤20.00 | 1.20±0.15 | 50 | |||||||
| Φ50 | 51.0±0.7 | 0.55±0.15 | ≤25.00 | 1.20±0.15 | 25 | |||||||
| Φ60 | ≥60 | 0.60±0.15 | ≤30.00 | 1.5±0.2 | 25 | |||||||
| Φ70 | ≥70 | 0.65±0.15 | ≤35.00 | 1.6±0.2 | 25 | |||||||
| Φ80 | ≥80 | 0.70±0.15 | ≤40.00 | 1.7±0.2 | 25 | |||||||
| Φ90 | ≥90 | 0.75±0.15 | ≤45.00 | 1.9±0.2 | 25 | |||||||
| Φ100 | ≥100 | 0.80±0.20 | ≤50.00 | 2.10±0.2 | 25 | |||||||
| Property Item | Test Method | Typical Value | ||||||||||
| Tensile Strength | ASTM D2671 | ≥10.4Mpa | ||||||||||
| Elongation At Break | ASTM D2671 | ≥200% | ||||||||||
| Dielectric Strength | IEC 243 | ≥15kv/mm | ||||||||||
| Volume Resistivity | IEC 93 | ≥1 x 1014Ω·cm | ||||||||||
| Tensile Strength After Aging | UL224 158ºC x 168hr | ≥7.3 | ||||||||||
| Elongation After Aging | UL224 158ºC x 168hr | ≥100% | ||||||||||
| Heat Shock | UL224 250ºC x 4hr | No cracking | ||||||||||
| Flame retardance | UL224 | VW-1 | ||||||||||